Resin for 3D printer FormFutura Platinum LCD Series 0.5kg - Solid White

Product Code: AN-18246
Availability: Temporarily Out Of Stock
51.40€
Ex Tax: 42.48€

Solid white photopolymer resin used in open source 3D printers equipped with an LCD and DLP projector. It is cured by light with wavelength ranging from 385 nm to 420 nm. The product emits small amounts of unpleasant odour during the printing process. Finished models obtained from FormFutura Platinum LCD Series are characterized by a high level of detail and smooth texture. A characteristic feature of resins from this line is short exposure time. Package contains 0.5 kg of product.


Main features of the Platinum LCD Series resins

  • Produces low odor during printing
  • Resistance to weather conditions and UV radiation
  • Faster printing due to short exposure time
  • Produce high-resolution, highly detailed models
  • Offers vibrant, long-lasting colors without discoloration (available in translucent and opaque versions)
  • Resins have low shrinkage and water absorption (absorbency)
  • Used in model and figure printing and functional prototyping

Steps to be taken before starting printing

  • Shake the bottle for at least 2 minutes before each use.
  • Then leave the resin for about 10 minutes to let the air bubbles escape from the resin
  • After printing, unused resin can be transferred from the printer tank to the bottle

Final processing of the finished 3D printout

  • Ready model should be rinsed in isopropyl alcohol (IPA) or bioethanol for about 5 minutes.
  • The manufacturer recommends the use of ultrasonic cleaner.
  • Before further curing check if the model is completely dry after rinsing
  • Place the rinsed parts in a well-ventilated room for at least 30 min. (Compressed air can also be used for at least 2 minutes).
  • Cure the objects in a special chamber for 20 to 30 minutes at 65°C
  • Recommended curing wavelength is from 300 nm to 410 nm
  • When grinding resin, respiratory protection is absolutely necessary


Specification:

  • Viscosity: 500 cps at 25°C
  • Density: 1.18 g/cm2
  • Glass transition temperature (Tg) 51°C
  • Water absorption 0,4%
  • Impact strength (IZOD) 18 J/m
  • Tensile Strength 45 MPa
  • Tensile Resilience 1000 MPa
  • Elongation at tension 8%
  • Bending Strength 66 MPa
  • Elasticity 1800 MPa
  • Shore Hardness 82