Copymaster PLA - 1.75mm - 1kg - Deep Black

Brand: Copymaster3D
Product Code: PRM-8350
Availability: Temporarily Out Of Stock
24.90€
Ex Tax: 20.58€

PLA from Copymaster3D is a high-quality filament that can be used in many applications when it comes to 3D printing. We also offer Copymaster3D in a wide range of colors so you can be sure of finding your personal favorite. PLA is based on polylactic acid and is fully biodegradable and emits no toxic fumes. This means that you don’t have to worry about using the filament indoors with children or pets nearby. Copymaster3D PLA also has the benefit of very low shrinkage, this means that you will have very accurate prints, but also that the risk of warping is very low. Even though a heated build platform isn´t required we do recommend it as you will get the best adhesion. To be extra sure that the print sticks well to the build plate we recommend that you use PrimaFIX. It will make the prints stick better but will also make it much easier to remove the print from the build surface once it cools off. If you use the heated bed we recommend a temperature between 30 - 60 °C

Main features:

  • Outstanding price-to-performance ratio
  • PLA is the easiest filament to print with
  • Good for professionals as well as for beginners
  • Good for making high-resolution parts
  • No shrinking after cooling
  • Low risk of warping
  • Low melting point
  • A wide range of attractive colors is available
  • No toxic fumes
  • Biodegradable

Specification:

  • Filament Type: PLA
  • Diameter: 1,75 mm
  • Tolerance: 0,05 mm
  • Weight: 1,00 kg
  • Length: 335 m
  • Color: Deep Black
  • Recommended Printing Temp. Min.: 190 ºC
  • Recommended Printing Temp. Max.: 220 ºC
  • Recommended Printbed Temperature Min.: 0 ºC
  • Recommended Printbed Temperature Max.: 45 ºC
  • Recommended Printing Speed Min.: 40 mm/s
  • Recommended Printing Speed Max.: 150 mm/s
  • Recommended Fan Speed Min: 60%
  • Recommended Fan Speed Max: 100%
  • Specific gravity: 1,24 g/cm3
  • Heat deflection temp: 50 °C
  • Tensile strength: 45 MPa
  • Elongation at yield: 5,3%
  • Elongation at break: 13,3%
  • Flexural Strenght: 63,64%
  • Flexural Modulus: 2157
  • Impact Strength: 17 KJ/m2